743 NYLENE | Alldatasheet
Document overview
- Manufacturer or author: Provided By alldatasheet.com(free datasheet download site)
- PDF pages: 2
Technical content
NYLENE USA NYLENE CANADA ULC. ISO/IEC 17025 & ISO 9001:2015 Accredited Facilities en 1421 Hwy 136 West 200 McNab Street Product is manufactured in Henderson, KY one) Nylene Henderson, Kentucky 42420 Arnprior, Ontario K7S 3P2 Web: www.nylene.com | Email: info@nylene.com Phone: 270-826-7641 Phone: 613-623-3191 TDS Ref ID: 1228 Toll-free: 800-626-7050 Toll-free: 800-267-7394 Date Updated October 11, 2024 Nylene® 743 Technical Data Sheet Resin Type: * Nylon 6 tesin Type: ryion Processing Method{(s): Description: _ = Designed for excellent cold temperature impact. * Extrusion * High impact modified nylon 6 suitable for both molding and extrusion. * Tubing & Profile * Parts molded from 743 have excellent impact strength right out of the mold without post conditioning. = Smooth Tubing * Outstanding high strength and high cold temperature impact. * Cylinder temperatures should be in the 435 - 525°F range. Fillers/Reinforcements: * Unfilled Properties ASTM/ISO Unit English sl Procedure Form(s)/Color(s): Mechanical = Pellets Notched Izod @ -40°C D256 ft-b/in (u/m) 35 187 Elongation D638 % 150 Features: TROT * Cold temperature resistance * High impact Melt Point Iso 1357 - D °F (°C) 426 219 3418 End Uses: Physical * Automotive Specific Gravity D792 nla 1.08 1 = Fuel Applications eT = Fuel Reservoirs = Fuel Tanks Tensile Strength D638 psi (MPa) 7700 53 * Lawn and Garden Flexural Modulus 790 psi (MPa) 230000 1,586 Disclai Notched Izod Impact D256 ft-lbyin (Jim) No isclaimer Breaks Nylene does not guarantee the accuracy of this information or the suitability of this ‘ARM Drop Impact, C.T., -30°C ARM fetb (N) 150 667 product for any given application or usage Drop Weight Impact @ RT ‘ARM ft-lb (N) 150 667 situation. These values are based on test specimens and should not be used to ‘ARM Drop Impact, C.T., -40°C ARM field (N) 150 667 establish specification limits or fabricate tooling. Notes: Testing conducted on dry-as-molded specimens at 73°F (22.8°C} Recommended Processing Considerations: PAG Injection Molding - Impact Modified Pressure psi Injection 7-15,000 Hold 5-12,000 Back 0.50 Melt Temperature: Melt Temperature: Nylene® PAG melts at 428°F, (220°C) actual melt temperatures of 440-560°F (227- 293°C) are permissible, depending on residence time and shot size Mold Temperature: 120-200°F (49-93°C), highly filled grades require 180-200°F (82-93°C) to obtain the best overall surface appearance, higher temperatures will increase crystallinity. Residence Time: should not exceed 6 minutes if possible, less with higher melt temperatures Shot Size: should be between 25-75% of barrel capacity. Fill Rate: fast fill rates are suggested for best surface appearance.
Regrind Level: typically no more than 25% is recommended, with higher levels possible for unfilled grades depending on the end use requirements. Make certain regrind is properly dried to virgin moisture levels. Drying Temperature: 150-180°F (66-82°C) for 2-4 hours, Nylene® PAG should be dried to less than 0.20% moisture for ‘optimum performance. Drying longer than 4 hours or at higher temperatures may cause discoloration of the polymer or adversely affect important physical properties. moisture levels.