Supplier : Samsung electro-mechanics Samsung P/N: CL05A105KO5NNNC Product : Multi-layer Ceramic Capacitor Description : CAP, 1㎌, 16V, ±10%, X5R, 0402 CL 05 A 105 K O 5 N N N C ① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪ ① Series Samsung Multi-layer Ceramic Capacitor ② Size 0402 (inch code) L: 1.00 ± 0.05 mm W: ± 0.05 mm ③ Dielectric ⑧ Inner electrode ④ Capacitance 1 ㎌ Termination ⑤ Capacitance ±10 % Plating (Pb Free) tolerance ⑨ Product Normal ⑥ Rated Voltage 16 V ⑩ Special Reserved for future use ⑦ Thickness 0.50 ± 0.05 mm ⑪ Packaging Cardboard Type, 7" reel 0.50 X5R SPECIFICATION (Reference sheet) A. Samsung Part Number Sn 100% Cu Ni B. Samsung Reliability Test and Judgement condition Capacitance Within specified tolerance Tan δ (DF) 0.1 max. Insulation 10,000Mohm or 100Mohm㎌ Rated Voltage 60~120 sec. Resistance Whichever is Smaller Appearance No abnormal exterior appearance Microscope (×10) Withstanding No dielectric breakdown or of the rated voltage Voltage mechanical breakdown Temperature X5R Characterisitcs (From -55℃ to 85℃, Capacitance change should be within ±15%) Adhesive Strength No peeling shall be occur on the 500g·F, for 10±1 sec. of Termination terminal electrode Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm) with 1.0mm/sec. Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder is to be soldered newly 245±5℃, 3±0.3sec. (preheating : 80~120℃ for 10~30sec.) Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec. Soldering heat Tan δ, IR : initial spec. Judgement Test condition 250% 1㎑±10% 1.0±0.2Vrms *A capacitor prior to measuring the capacitance is heat treated at 150℃+0/-10℃, and maintained in ambient air for 24±2 hours.
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.) 2hours × 3 direction (x, y, z) Moisture Capacitance change : within ±12.5% With rated voltage Resistance Tan δ 0.2 max 40±2℃, 90~95%RH, 500+12/-0hrs IR : 500Mohm or 12.5 Mohm ㎌ Whichever is Smaller High Temperature Capacitance change : within ±12.5% Wit h of the rated voltage Resistance Tan δ 0.2 max Max. operating temperature IR : 1,000Mohm or 25Mohm ㎌ 1000+48/-0hrs Whichever is Smaller Temperature Capacitance change : within ±7.5% 1 cycle condition Cycling Tan δ, IR : initial spec. Min. operating temperature → 25℃ → Max. operating temperature → 25℃ 5 cycle test C. Recommended Soldering method : Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max ) Product specifications included in the specifications are effective as of March 1, 2013. Please be advised that they are standard product specifications for reference only. We may change, modify or discontinue the product specifications without notice at any time. So, you need to approve the product specifications before placing an order. 100% Judgement Test condition Should you have any question regarding the product specifications, please contact our sales personnel or application engineers.