Product Specification – January 16, 2017 V.9 DATA SHEET SURFACE-MOUNT CERAMIC MULTILAYER CAPACITORS High-Voltage NP0/X7R

1 KV TO 3 KV

RoHS compliant & Halogen Free

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification ORDERING INFORMATION - GLOBAL PART NUMBER, PHYCOMP CTC & 12NC All part numbers are identified by the series, size, tolerance, TC material, packing style, voltage, process code, termination and capacitance value. YYAAGGEEOO BBRRAANNDD oorrddeerriinngg ccooddee GLOBAL PART NUMBER (PREFERRED ) CC XXXX X X XXX X B X XXX (1) SIZE – INCH BASED (METRIC) 0805 (2012) / 1206 (3216) / 1210 (3225) / 1808 (4520) / 1812 (4532) (2) TOLERANCE C = ± 0.25 pF D = ± 0.5 pF G = ± 2% J = ± 5% K = ± 10% (3) PACKING STYLE R = Paper/PE taping reel; Reel 7 inch K = Blister taping reel; Reel 7 inch P = Paper/PE taping reel; Reel 13 inch F = Blister taping reel; Reel 13 inch C = Bulk case (4) TC MATERIAL NPO X7R (5) RATED VOLTAGE C = 1 KV D = 2 KV S = 2.5KV E = 3 KV (6) PROCESS N = NP0 B = Class 2 MLCC (7) CAPACITANCE VALUE 2 significant digits+number of zeros The 3rd digit signifies the multiplying factor, and letter R is decimal point Example: 121 = 12 x 101 = 120 pF SCOPE This specification describes High - Voltage NP0/X7R series chip capacitors with lead -free terminations.

APPLICATIONS

PCs, Hard disk, Game PCs Power supplies LCD panel ADSL, Modem

FEATURES

Nickel -barrier end termination RoHS compliant Halogen Free compliant

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification CONSTRUCTION The capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. This structure gives rise to a high capacitance per unit volume. The inner electrodes are connected to the two end terminations and finally covered with a layer of plated tin (NiSn). The terminations are lead -free. A cross section of the structure is shown in Fig.1. Fig. 1 Surface mounted multilayer ceramic capacitor construction TYPE L1 (mm) W (mm) T (MM) L2 / L3 (mm) L4 (mm) min. max. min. 0805 2.0 ± 0.20 1.25 ± 0.20 Refer to table 2 to 4 0.25 0.75 0.55 Table 1 For outlines see fig. 2 DIMENSION OOUUTTLLIINNEESS For dimension see Table 1 Fig. 2 Surface mounted multilayer ceramic capacitor dimension

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification CAPACITANCE RANGE & THICKNESS FOR NP0 Table 2 Sizes from 0805 to 1812 CAP. 0805 1206 1210 1808 1812

1 KV 1 KV 2 KV 1 KV 2 KV 1 KV 2 KV 3 KV 1 KV 2 KV 3 KV

1.2 nF 1.25± 0.2 1.5 nF 1.25± 0.2 1.8 nF 2.2 nF 2.7 nF 3.3 nF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-12 series is on request

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification Table 3 Sizes from 0805 to 1812 CAPACITANCE RANGE & THICKNESS FOR X7R CAP. 0805 1206 1210 1808 1812 1 KV 1 KV 2 KV 2.5KV 1 KV 2 KV 1 KV 2 KV 3 KV 1 KV 2 KV 3 KV 100 pF 150 pF 0.85± 0.1 1.6± 0.2 15 nF 1.25± 0.2 1.35± 0.15 22 nF 1.6± 0.2 1.35± 0.15 33 nF 1.6± 0.2 47 nF 68 nF 100 nF NOTE 1. Values in shaded cells indicate thickness class in mm 2. Capacitance value of non E-6 series is on request 3. For products with 5% tolerance, please contact local sales force before ordering

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification Table 5 THICKNESS CLASSES AND PACKING QUANTITY SIZE CODE THICKNESS CLASSIFICATION TAPE WIDTH QUANTITY PER REEL Ø 180 MM / 7 INCH Ø 330 MM / 13 INCH QUANTITY PER BULK CASE Paper Blister Paper Blister 0402 0.5 ± 0.05 mm 8 mm 10,000 --- 50,000 --- 50,000 0603 0.8 ± 0.1 mm 8 mm 4,000 --- 15,000 --- 15,000 0805 1206 1210 1,000 --- --- --- 500 --- --- --- 1808 1812

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification

ELECTRICAL CHARACTERISTICS

NNPP00//XX77RR DDIIEELLEECCTTRRIICC CCAAPPAACCIITTOORRSS;; NNIISSNN TTEERRMMIINNAATTIIOONNSS Unless otherwise stated all electrical values apply at an ambient temperature of 20±1 °C, an atmospheric pressure of 86 to 106 kPa, and a relative humidity of 63 to 67%. Table 6 DESCRIPTION VALUE Capacitance range 10 pF to 33 nF Capacitance tolerance NP0 C < 10 pF ± 0.25 pF, ± 0.5 pF Dissipation factor (D.F.) NP0 C < 30 pF ≤ 1 / ( 400 + 20C ) C ≥ 30 pF ≤ 0.1 % X7R ≤ 2.5 % Insulation resistance after 1 minute at Ur (DC) Rins ≥ 10 GΩ or Rins × C ≥ 500 seconds whichever is less Maximum capacitance change as a function of temperature (temperature characteristic/coefficient): NP0 ± 30 ppm/°C X7R ± 15% Operating temperature range: NP0/X7R –55 °C to +125 °C NOTE 1. ±5% tolerance of capacitance value isn't available for X7R full product range, please contact local sales force before ordering

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification Fig. 3 Typical temperature coefficient as a function of temperature Sample limits (broken lines). Requirement levels (dotted lines) HIGH-VOLTAGE NP0 Fig. 4 Typical tan δ as a function of temperature HIGH-VOLTAGE X7R Fig. 5 Typical capacitance change as a function of temperature X Fig. 6 Typical tan δ as a function of temperature

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification SOLDERING RECOMMENDATION Table 7 SOLDERING METHOD SIZE 0402 0603 0805 1206 ≥ 1210 Reflow Reflow only ≥ 1.0 µF ≥ 2.2 µF ≥ 4.7 µF Reflow only Reflow/Wave --- < 1.0 µF < 2.2 µF < 4.7 µF --- TEST TEST METHOD PROCEDURE REQUIREMENTS Mounting IEC 60384-

4.3 The capacitors may be mounted on printed-circuit boards or

4.4 Any applicable method using × 10 magnification In accordance with specification

Capacitance 4.5.1 Class 1: f = 1 MHz for C ≤ 1 nF, measuring at voltage 1 Vrms at 20 °C f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Class 2: f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C Within specified tolerance Dissipation Factor (D.F.)

4.5.2 Class 1:

f = 1 MHz for C ≤ 1 nF , measuring at voltage 1 Vrms at 20 °C f = 1 KHz for C > 1 nF, measuring at voltage 1 Vrms at 20 °C Class 2: f = 1 KHz for C ≤ 10 µF, measuring at voltage 1 Vrms at 20 °C In accordance with specification Insulation Resistance

4.5.3 Ur ≤ 500 V: At Ur for 1 minute

Ur > 500 V: At 500 V for 1 minute In accordance with specification TESTS AND REQUIREMENTS Table 8 Test procedures and requirements

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification TEST TEST METHOD PROCEDURE REQUIREMENTS Temperature Coefficient

4.6 Capacitance shall be measured by the steps shown

in the following table. The capacitance change should be measured after 5 min at each specified temperature stage. Step Temperature(℃) a 25± 2 b Lower temperature± 3℃ c 25± 2 d Upper Temperature± 2℃ e 25± 2 (1) Class I Temperature Coefficient shall be calculated from the formula as below Temp, Coefficient = 610T xC1 C1-C2 Δ [ppm/℃] C1: Capacitance at step c C2: Capacitance at 125℃ (2) Class II Capacitance Change shall be calculated from the formula as below ∆C = C1-C2 x 100% C1: Capacitance at step c C2: Capacitance at step b or d <General purpose series> Class1: ∆ C/C: ± 30ppm Class2: X7R: ∆ C/C: ±15% <High Capacitance series> Class2: X7R/X5R: ∆ C/C: ±15% Adhesion IEC 60384- 4.7 A force applied for 10 seconds to the line joining the terminations and in a plane parallel to the substrate Force size ≥ 0603: 5N Bending Strength 4.8 Mounting in accordance with IEC 60384-22 paragraph 4.3 No visible damage Conditions: bending 1 mm at a rate of 1 mm/s, radius jig 5 mm ∆C/C Class 1: NP0: within ± 1% or 0.5 pF, whichever is greater Class2: X7R: ± 10%

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification TEST TEST METHOD PROCEDURE REQUIREMENTS Resistance to Soldering Heat 4.9 Precondition: 150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature Preheating: for size ≤ 1206: 120 °C to 150 °C for 1 minute Preheating: for size >1206: 100 °C to 120 °C for 1 minute and 170 °C to 200 °C for 1 minute Solder bath temperature: 260 ± 5 °C Dipping time: 10 ± 0.5 seconds Recovery time: 24 ±2 hours Dissolution of the end face plating shall not exceed 25% of the length of the edge concerned ∆C/C Class 1: NP0: within ±0.5% or 0.5 pF, whichever is greater Class2: X7R: ± 10% D.F. within initial specified value Rins within initial specified value Solderability 4.10 Preheated to a temperature of 80 °C to 140 °C and maintained for 30 seconds to 60 seconds. 1. Temperature: 235± 5°C / Dipping time: 2 ± 0.5 s 2. Temperature: 245± 5°C / Dipping time: 3 ± 0.5 s (lead free)Depth of immersion: 10mm The solder should cover over 95% of the critical area of each termination Rapid Change of Temperature IEC 60384-

4.11 Preconditioning;

150 +0/–10 °C for 1 hour, then keep for 24 ± 1 hours at room temperature 5 cycles with following detail: 30 minutes at lower category temperature 30 minutes at upper category temperature Recovery time 24 ± 2 hours No visual damage ∆C/C Class 1: NP0: within ± 1% or 1 pF, whichever is greater Class2: X7R: ± 15% D.F. meet initial specified value Rins meet initial specified value Damp Heat 4.13 1. Preconditioning, class 2 only: 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp 2. Initial measure: Spec: refer to initial spec C, D, IR 3. Damp heat test: 500 ± 12 hours at 40 ±2 °C; 90 to 95% R.H. 4. Recovery: Class 1: 6 to 24 hours Class 2: 24 ± 2 hours 5. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be preconditioned according to “IEC 60384 4.1” and then the requirement shall be met. No visual damage after recovery ∆C/C Class 1: NP0: within ± 2% or 1 pF, whichever is greater Class2: X7R: ± 15% D.F. Class 1: NP0: ≤ 2 x specified value Class2: X7R: ≥ 25 V: ≤ 5% Rins Class 1: NP0: ≥ 2,500 MΩ or Rins x Cr ≥ 25s whichever is less Class2: X7R: ≥ 500 MΩ or Rins x Cr ≥ 25s whichever is less

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification TEST TEST METHOD PROCEDURE REQUIREMENTS Endurance IEC 60384- 4.14 1. Preconditioning, class 2 only: 150 +0/-10 °C /1 hour, then keep for 24 ± 1 hour at room temp 2. Initial measure: Spec: refer to initial spec C, D, IR Endurance test: Temperature: NP0/X7R: 125 °C Specified stress voltage applied for 1,000 hours. High-Voltage series follows the stress conditions below: Voltage NPO X7R ≤ 100V 2.0 x Ur 2.0 x Ur 200/250V 1.5 x Ur 1.5 x Ur 500/630V 1.3 x Ur 1.2 x Ur ≥ 1KV 1.2 x Ur 1.1 x Ur 3. Recovery time: 24 ± 2 hours 4. Final measure: C, D, IR P.S. If the capacitance value is less than the minimum value permitted, then after the other measurements have been made the capacitor shall be preconditioned according to “IEC 60384 4.1” and then the requirement shall be met. No visual damage ∆C/C Class1: NP0: within ± 2% or 1 pF, whichever is greater Class2: X7R: ± 15% D.F. Class1: NP0: ≤ 2 x specified value Class2: X7R: ≥ 25 V: ≤ 5% Rins Class1: NP0: ≥ 4,000 MΩ or Rins x Cr ≥ 40s whichever is less Class2: X7R: ≥ 1,000 MΩ or Rins x Cr ≥ 50s whichever is less Voltage Proof Specified stress voltage applied for 1~5 seconds Ur ≤ 100 V: series applied 2.5 Ur

100 V < Ur ≤ 200 V series applied

(1.5 Ur + 100)

200 V < Ur ≤ 500 V series applied

(1.3 Ur + 100) Ur > 500 V: 1.3 Ur Ur ≥ 1KV: 1.2 Ur Charge/Discharge current less than 50mA No breakdown or flashover

www.yageo.com Jan. 16, 2017 V.9 Surface-Mount Ceramic Multilayer Capacitors Product specification

REVISION HISTORY

REVISION DATE CHANGE NOTIFICATION DESCRIPTION Version 9 Jan. 16, 2017 - - Product range updated Version 8 Oct. 12, 2015 - - Product range updated Version 7 May 21, 2014 - - Product range updated Version 6 Jun. 17, 2012 - - Product range updated Version 5 Sep 25, 2012 - - Product range updated Version 4 Aug 08, 2011 - - Product range updated Version 3 Jan 19, 2011 - - Dimension updated - Add NP0 0805 1KV Version 2 Feb 02, 2010 - - Change to dual brand datasheet that describe High-Voltage NP0/X7R series with RoHS compliant - Replace the high voltage part of pdf files: UP-NP0X7R_HV_1K-to-4KV_1 and UY-NP0X7R_HV_1K-to-4KV_1 - Description of "Halogen Free compliant" added - Product range updated - Define global part number - Test method and procedure updated Version 1 Sep 30, 2005 - - Thickness revised Version 0 Sep 12, 2005 - - New