October, 2014 3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Product Description A fast curing, one-part polyurethane that chemically reacts with moisture to deliver strong, exible bonds to wood, gelcoat and berglass. It forms watertight, weather-resistant seals on joints and boat hardware above and below the waterline. In addition, its exibility allows for dissipation of stress caused by shock, vibration, swelling or shrinking. Product Features
- Fast cure formula • One component, moisture curing • Allows for disassembly • Bonds dissimilar materials • Extended shelf life • Adheres to a wide variety of substrates • Non-sagging • Permanently elastic
3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Technical Information Note The following technical information and data should be considered representative or typical only and should not be used for specication purposes. Typical Uncured Physical Properties Property Values Density 9.75 lb/gal Consistency Caulkable, non-sag paste Typical Mixed Physical Properties Property Values Test Condition Tack Free Time 1 to 2 h Room Temperature Rate of Cure 4 mm per 24 hr 3/16 in per 24 hr Room Temperature Typical Cured Characteristics Shore A Hardness: 40 MethodsASTM C661 Typical Performance Characteristics Property Values Method Tensile Strength 1.24 MPa 180 lb/in² ASTM D412 Elongation at Break >400 % ASTM D412 Service Temperature Range -40 to 88 °C -40 to 190 °F Table continued on next page OverlapShearStrength Dwell/CureTime Substrate SubstrateNotes Failure mode Notes TestCondition 11.6 kg/cm² 165 lb/in² Room Temperature Fir Woods Cohesive One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive.
3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Typical Performance Characteristics (continued) Table continued on next page OverlapShearStrength Dwell/CureTime Substrate SubstrateNotes Failure mode Notes TestCondition 7.2 kg/cm² 100 lb/in² Room Temperature Stainless Steel Metals Mixed Cohesive/AdhesiveOne inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive. 7 kg/cm² 100 lb/in² Room Temperature Aluminum Metals Mixed Cohesive/AdhesiveOne inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive. 3.9 kg/cm² 55 lb/in² Room Temperature Acrylic (PMMA) Plastics/PolymersAdhesive One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive. 6.6 kg/cm² 95 lb/in² Room Temperature Nylon Plastics/PolymersAdhesive One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive. 7 kg/cm² 100 lb/in² Room Temperature ABS Plastics/PolymersAdhesive One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive. 2 kg/cm² 25 lb/in² Room Temperature Polypropylene (PP) Plastics/PolymersAdhesive One inch (2.54 cm) overlap specimens (0.093 inch [0.2362 cm] thickness) Cohesive – Adhesive/Sealant fails before adhesive/sealant releases from substrate. This is the desired mode. Adhesive Failure – Adhesive/Sealant releases from substrate. Desirable failure mode is cohesive.
3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Typical Performance Characteristics (continued) OverlapShearStrength Dwell/CureTime Substrate SubstrateNotes Failure mode Notes TestCondition Room Temperature Room Temperature 11.6 kg/cm² 165 lb/in² Fiber-Reinforced Plastic Room Temperature 1.5 kg/cm² 20 lb/in² Low Density Polyethylene (LDPE) Room Temperature Room Temperature Property: Overlap Shear Strength Typical Physical Properties Solids Content by Weight: 100 % Handling/Application Information Directions for Use Surface Preparation:
3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Handling/Application Information (continued)
3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Storage and Shelf Life Polyurethane sealants and adhesive sealants must be stored in a controlled environment to maximize shelf life. Store the products in the original unopened containers below 77°F (25C). When stored at recommended conditions, the shelf life of cartridges and sausage packs is 12 months from the date of manufacture. For 5 and 55 gallon containers, the shelf life is 6 months from date of manufacture. Trademarks 3M and Scotch-Brite are trademarks of 3M Company. References Property Values 3m.com Product Page https://www.3m.com/3M/en_US/company-us/all-3m-products/~/3M-Marine-Adhesive-Sealant-Fast-Cure-4200FC?N=5002385+3291170224&rt=rud Safety Data Sheet (SDS) https://www.3m.com/3M/en_US/company-us/SDS-search/results/?gsaAction=msdsSRA&msdsLocale=en_US&co=ptn&q=4200 This Industrial Adhesives and Tapes Division product was manufactured under a 3M quality system registered to ISO 9001 standards. Refer to Product Label and Material Safety Data Sheet for health and safety information before using this product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501.
3M™ Marine Adhesive Sealant Fast Cure 4200: 06560 • 06564 • 05260 Information 3M United States 3M Center St. Paul, MN 55144-1000 800-362-3550 www.3M.com Please recycle. © 3M 2021. All Rights Reserved. The brands listed above are trademarks of 3M Technical Information: The technical information, guidance, and other statements contained in this document or otherwise provided by 3M are based upon records, tests, or experience that 3M believes to be reliable, but the accuracy, completeness, and representative nature of such information is not guaranteed. Such information is intended for people with knowledge and technical skills sucient to assess and apply their own informed judgment to the information. No license under any 3M or third party intellectual property rights is granted or implied with this information. Warranty, Limited Remedy, and Disclaimer: Unless a dierent warranty is specically stated on the applicable 3M product packaging or product literature (in which case such warranty governs), 3M warrants that each 3M product meets the applicable 3M product specication at the time 3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY, FITNESS FOR A PARTICULAR PURPOSE, OR ARISING OUT OF A COURSE OF DEALING, CUSTOM, OR USAGE OF TRADE. If a 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M’s option, replacement of the 3M product or refund of the purchase price. Limitation of Liability: Except for the limited remedy stated above, and except to the extent prohibited by law, 3M will not be liable for any loss or damage arising from or related to the 3M product, whether direct, indirect, special, incidental, or consequential (including, but not limited to, lost prots or business opportunity), regardless of the legal or equitable theory asserted, including, but not limited to, warranty, contract, negligence, or strict liability.